Fullerene Fragment Restructuring: How Spatial Proximity Shapes Defect-Rich Carbon Electrocatalysts
Ning Li, Kun Guo*, Mengyang Li, Xiudi Shao, Zhiling Du, Lipiao Bao, Zhixin Yu, and Xing Lu*
J. Am. Chem. Soc. 2023
https://doi.org/10.1021/jacs.3c06456
Abstract
Fullerene transformation emerges as a powerful route to construct defect-rich carbon electrocatalysts, but the carbon bond breakage and reformation that determine the defect states remain poorly understood. Here, we explicitly reveal that the spatial proximity of disintegrated fullerene imposes a crucial impact on the bond reformation and electrocatalytic properties. A counterintuitive hard-template strategy is adopted to enable the space-tuned fullerene restructuring by calcining impregnated C60 not only before but also after the removal of rigid silica spheres (∼300 nm). When confined in the SiO2 nanovoids, the adjacent C60 fragments form sp3 bonding with adverse electron transfer and active site exposure. In contrast, the unrestricted fragments without SiO2 confinement reconnect at the edges to form sp2-hybridized nanosheets while retaining high-density intrinsic defects. The optimized catalyst exhibits robust alkaline oxygen reduction performance with a half-wave potential of 0.82 V via the 4e– pathway. Copper poisoning affirms the intrinsic defects as the authentic active sites. Density functional theory calculations further substantiate that pentagons in the basal plane lead to localized structural distortion and thus exhibit significantly reduced energy barriers for the first O2 dissociation step. Such space-regulated fullerene restructuring is also verified by heating C60 crystals confined in gallium liquid and a quartz tube.